| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 873873 | Journal of Biomechanics | 2009 | 6 Pages |
Understanding the off-axis behavior of trabecular yield strains may lend unique insight into the etiology of fractures since yield strains provide measures of failure independent of elastic behavior. We sought to address anisotropy of trabecular yield strains while accounting for variations in both density and anatomic site and to determine the mechanisms governing this behavior. Cylindrical specimens were cored from vertebral bodies (n=22, BV/TV=0.11±0.02) and femoral necks (n=28, BV/TV=0.22±0.06) with the principal trabecular orientation either aligned along the cylinder axis (on-axis, n=22) or at an oblique angle of 15° or 45° (off-axis, n=28). Each specimen was scanned with micro-CT, mechanically compressed to failure, and analysed with nonlinear micro-CT-based finite element analysis. Yield strains depended on anatomic site (p=0.03, ANOVA), and the effect of off-axis loading was different for the two sites (p=0.04)—yield strains increased for off-axis loading of the vertebral bone (p=0.04), but were isotropic for the femoral bone (p=0.66). With sites pooled together, yield strains were positively correlated with BV/TV for on-axis loading (R2=58%, p<0.0001), but no such correlation existed for off-axis loading (p=0.79). Analysis of the modulus-BV/TV and strength-BV/TV relationships indicated that, for the femoral bone, the reduction in strength associated with off-axis loading was greater than that for modulus, while the opposite trend occurred for the vertebral bone. The micro-FE analyses indicated that these trends were due to different failure mechanisms for the two types of bone and the different loading modes. Taken together, these results provide unique insight into the failure behavior of human trabecular bone and highlight the need for a multiaxial failure criterion that accounts for anatomic site and bone volume fraction.