Thermal fatigue cracking of surface engineered hot work tool steels

Generally, all surface treatments decreased the resistance against surface cracking as compared to the reference materials. The reason is that the engineering processes influence negatively on the mechanical properties of the tool materials. Of the processes evaluated, duplex treatment was the least destructive. It gave a lower crack density than the reference steel, but the diffusion layer is more susceptible to crack propagation. In addition, the single-layered CrN coating showed almost comparable thermal fatigue cracking resistance as the reference material. Finally, the resistance against thermal crack propagation of surface engineered tool steels is primarily determined by the mechanical properties of the substrate material.