Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
10159710 | Acta Biomaterialia | 2012 | 7 Pages |
Abstract
The microstructure and mechanical properties of as-cast Co-(20-33)Cr-5Mo-N alloys were investigated to develop ductile Co-Cr-Mo alloys without Ni addition for dental applications that satisfy the requirements of the type 5 criteria in ISO 22674. The effects of the Cr and N contents on the microstructure and mechanical properties are discussed. The microstructures were evaluated using scanning electron microscopy with energy-dispersive X-ray spectroscopy (EDS), X-ray diffractometry (XRD), and electron back-scattered diffraction pattern analysis. The mechanical properties were evaluated using tensile testing. The proof strength and elongation of N-containing 33Cr satisfied the type 5 criteria in ISO 22674. ε-phase with striations was formed in the N-free (20-29)Cr alloys, while there was slight formation of ε-phase in the N-containing (20-29)Cr alloys, which disappeared in N-containing 33Cr. The lattice parameter of the γ-phase increased with increasing Cr content (i.e. N content) in the N-containing alloys, although the lattice parameter remained almost the same in the N-free alloys because of the small atomic radius difference between Co and Cr. Compositional analyses by EDS and XRD revealed that in the N-containing alloys Cr and Mo were concentrated in the cell boundary, which became enriched in N, stabilizing the γ-phase. The mechanical properties of the N-free alloys were independent of the Cr content and showed low strength and limited elongation. Strain-induced martensite was formed in all the N-free alloys after tensile testing. On the other hand, the proof strength, ultimate tensile strength, and elongation of the N-containing alloys increased with increasing Cr content (i.e. N content). Since formation of ε-phase after tensile testing was confirmed in the N-containing alloys the deformation mechanism may change from strain-induced martensite transformation to another form, such as twinning or dislocation slip, as the N content increases. Thus the N-containing 33Cr alloy with large elongation is promising for use in dentures with adjustable clasps through one piece casting.
Related Topics
Physical Sciences and Engineering
Chemical Engineering
Bioengineering
Authors
Keita Yoda, Suyalatu Suyalatu, Atsushi Takaichi, Naoyuki Nomura, Yusuke Tsutsumi, Hisashi Doi, Shingo Kurosu, Akihiko Chiba, Yoshimasa Igarashi, Takao Hanawa,