Electrocatalyst stability is an important factor influencing the performance of polymer electrolyte membrane (PEM) fuel cells and is essential in maintaining the cell output. The aim of this work was to elucidate factors which influence the stability of platinum supported onto graphitic nanofibres (Pt/GNFs) and to compare the performance of these materials with the commonly used Pt/Vulcan electrocatalyst. Platinum nanoparticles (average diameter of 6.9 nm) were supported on GNFs which were prepared by chemical vapour deposition over an unsupported nickel oxide (NiO) catalyst precursor. The performance of Pt/GNFs based electrodes were studied by cyclic voltammetry and a single-cell fuel cell test and were compared with a commercially available carbon nanostructure, Vulcan XC-72, which was also impregnated with Pt nanoparticles. Characterisation of the pre- and post-operation of the Pt/GNFs by XRD and TEM showed that structural changes of the Pt had occurred during testing. It was found that the average diameter of each grain and the degree of agglomeration among particles was increased, creating elongated clusters of Pt along the carbon fibre. Analysis of electrocatalyst post-operation also identified that the sulphate from the Nafion membrane was reacting with the Pt surface forming platinum sulphide (PtS). These phases were confirmed by the presence of low intensity, but sharp XRD peaks, attributed to a few large diameter particles (49 nm). These two factors resulted in current density dropping from 0.2 A/cm2 to 0.1 A/cm2 (at 0.70 V) over a 25 h test period.