Preparation and characterization of sulfonated poly(tetra phenyl ether ketone sulfone)s for proton exchange membrane fuel cell

Sulfonated poly(tetra phenyl ether ketone sulfone)s SPTPEKS were successfully synthesized for proton exchange membrane. Poly(tetra phenyl ether ketone sulfone)s PTPEKS were prepared by the 4,4′-dihydroxydiphenylsulfone with 1,2-bis(4-fluorobenzoyl)-3,4,5,6-tetraphenylbenzene (BFBTPB) and 4,4′-difluorodiphenylsulfone, respectively, at 210 °C using potassium carbonate in sulfolane. PTPEKS were followed by sulfonation using chlorosulfonic acid and concentrated sulfuric acid at two stage reactions. Different contents of sulfonated unit of SPTPEKS (17, 20, 23 mol% of BFBTPB) were studied by FT-IR, 1H NMR spectroscopy, and thermo gravimetric analysis (TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymers with water. The ion exchange capacity (IEC) and proton conductivity of SPTPEKS were evaluated with increase of degree of sulfonation. The water uptake of synthesized SPTPEKS membranes exhibit 25–61% compared with 28% of Nafion 211®. The SPTPEKS membranes exhibit proton conductivities (25 °C) of 11.7–25.3 × 10−3 S/cm compared with 33.7 × 10−3 S/cm of Nafion 211®.

► Aromatic polymers were selectively sufonated on multi-phenyl at side chain. ► The polymer membranes showed good proton conductivity with high IEC. ► The polymer membranes exhibited similar fuel cell performance as Nafion 211.