For the first time, simultaneous production of hydrogen and nanocarbon via catalytic decomposition of methane over Ni-loaded mesoporous Ce-MCM-41 catalysts was investigated. The catalytic performance of the Ni/Ce-MCM-41 catalysts is very stable and the reaction activity remained almost unchanged during 1400 min steam on time at temperatures 540, 560 and 580 °C, respectively. The methane conversion level over these catalysts reached 60–75% with a 100% selectivity towards hydrogen. TEM observations revealed that most of the Ni particles located on the tip of the carbon nanofibers/nanotubes in the used catalysts, keeping their exposed surface clean during the test and thus remaining active for continuous reaction without obvious deactivation. Two kinds of carbon materials, graphitic carbon (Cg) as major and amorphous carbon (CA) as minor were produced in the reaction, as confirmed by XRD analysis and TEM observations. Carbon nanofibers/nanotubes had an average diameter of approximately 30–50 nm and tens micrometers in length, depending on the reaction temperature, reaction time and Ni particle diameter. Four types of carbon nanofibers/nanotubes were detected and their formations greatly depend on the reaction temperature, time on steam and degree of the interaction between the metallic Ni and support. The respective mechanisms of the formation of nanocarbons were postulated and discussed.