| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 1565397 | Journal of Nuclear Materials | 2013 | 8 Pages |
Irradiation behavior of ODS steel cladding tubes was evaluated for the further progress in understanding of the neutron-irradiation effects on ODS steel.Two types of ODS (9Cr–ODS_F/M, 12Cr–ODS_F) steel cladding tubes with differences in basic compositions and matrix phases were irradiated in JOYO. Post-irradiation examination data concerning hardness, ring tensile property, and microstructure were obtained.Hardness measurement after irradiation showed that there was an apparent irradiation temperature dependence on hardness for 9Cr–ODS_F/M steel whereas no distinct temperature dependence for 12Cr–ODS_F steel. Also, there was no significant change in tensile strengths after irradiation below 923 K, but those above 1023 K up to 6.6 × 1026 n/m2 (E > 0.1 MeV) were decreased by about 20%. TEM observations showed that the radiation-induced defect cluster formation during irradiation was suppressed because of high density sink site for defect such as initially-existed dislocation, and precipitate interfaces. In addition, oxide particles were stable up to the maximum doses of this irradiation test.