Influence of impurities on the evolution of vacancy-type defects in neutron-irradiated nickel

In order to investigate the effect of impurities on vacancy defect evolution in nickel, specimens with high (5N) and technical (3N) purity were neutron-irradiated at ∼330 K in the IVV-2M reactor (Russia) to fluencies in the range of 1 × 1021–1 × 1023 n/m2 (E > 0.1 MeV) corresponding to displacement dose levels in the range of about 0.0001–0.01 dpa and subsequently stepwise annealed to about 900 K. The specimens of Ni with different purities were characterized both in as-irradiated state as well as after post-irradiation annealing by positron annihilation spectroscopy. The formation of three-dimensional vacancy clusters (3D-VCs) in cascades was observed under neutron irradiation. The density and size of 3D-VCs depended not only on dose level, but also on purity. The population of 3D-VCs in the technical Ni is lower than that in the high-purity Ni. 3D-VCs collapse into secondary-type clusters (stacking fault tetrahedra (SFTs) and vacancy loops) during stepwise annealing at 350–450 K (stage III in Ni). The suppression of secondary cluster formation in 3N Ni is attributed to an effective vacancy interaction with impurity carbon atoms, which based on a relatively large vacancy–carbon atom binding energy (0.32–0.35 eV). The trapping of vacancies released at the collapse of 3D-VCs by the interstitial impurity atoms dominates at low irradiation dose level (10−4 dpa). Thus, we found that carbon impurity atoms have strong effects both on the primary vacancy-type defect aggregation and on the secondary vacancy clusters and complexes formation.

► We study, by means of PAS, the effects of purity on damage evolution in neutron-irradiated Ni at 330 K. ► Impurity carbon atoms in solution decrease the cascade efficiency during irradiation. ► C–V complexes are formed on the recovery stage III in impure Ni irradiated with 10−4 dpa. ► The formation of V-loops and SFTs dominate on stage III with increasing dose level. ► The thermal stability of SFTs in impure Ni is similar to that in pure Ni.