The silver colloidal solutions were prepared by in situ synthesis technique in the presence of the Polymethyl Methacrylate, which was polymerized by reversible addition-fragmentation transfer. The UV–VIS spectra and transmission electron microscopy had shown the formation of sphere silver nanoparticles with average size of 10 nm. Nonlinear optical properties as a function of silver concentration were studied using Z-scan technique with 13 ns pulse duration at 532 nm. The optical nonlinearity enhancement was observed by increasing the concentration. The third-order nonlinear susceptibility χ(3) was measured to 1.045 × 10−11 esu when the concentration was 2.13 mg/ml. Besides, the sample was founded to exhibit a shift from saturable absorption to reverse saturable absorption at higher incident laser energy. The reverse saturable absorption was observed to be responsible for the optical limiting characteristics in our experiments.