Nano-Ag complexes prepared by γ-radiolysis and their structures and physical properties

In this study, nano-silver (nano-Ag) complexes showing different properties have been synthesized as follows. Polypyrrolidone (PVP)-stabilized silver colloids (NAg), nano-Ag bound to silica (SiO2) (NSS), and nano-Ag bound to a complex of SiO2 and polyaniline (PANI) (NSSPAI) were prepared via γ-irradiation at room temperature. NAg and NSS used PVP as a colloidal stabilizer, while NSSPAI did not use PVP as a colloidal stabilizer. Interesting bonding properties occurred in the nano-Ag complex and anticipated structural changes were clearly shown through a surface analysis of x-ray photoelectron spectroscopy (XPS). The morphologies by field emission-scanning electron microscopy (FE-SEM) analysis showed that nano-Ag complexes have various particle sizes ranging from 10 to 30 nm. NSS (average, 10 nm) and NSSPAI (average, 30 nm) showed a uniformly spherical shape and size, while NAg did not. From the reflection peaks in the x-ray diffraction (XRD) patterns, surface crystallinity of the nano-Ag complexes was indicated to be in the same degree as that of NSSPAI>NSS>NAg. Also, in the contact angle (CA) determination, surface hydrophobicity of NSSPAI was stronger than those of NSS and NAg, relatively. The different nano-Ag complexes prepared by γ-irradiation can be applicable in various industry fields due to the increase in specific property.

► Nano-Ag complexes showing different properties have been synthesized via γ-irradiation. ► Nano-Ag colloid (NAg), nano-Ag bound to SiO2 (NSS), nano-Ag bound to SiO2 and PANI complex (NSSPAI). ► Nano-Ag complexes were the same based on Ag metal. ► Results clearly showed fascinating/different physical properties. ► Different nano-Ag complexes can be applicable in various industry fields.