Cerium/aluminum correlation in aluminosilicate glasses and optical silica fiber preforms

Al presence induces modifications on Ce local environment, and thus variations of the distance between Ce3 + and its ligands, and/or to variations of the covalency of the bonds. Absorption bands in the UV region, ascribed to Charge-transfer (CT) bands, in our samples, occur only for low amount of Ce4 + (Ce3 +/ΣCe > 0.85 ± 0.07). Indeed, in silicate and aluminosilicate glasses the higher amount of Ce4 + does not give rise to UV absorption bands ascribed to CT processes, whereas, in fiber preforms, Ce3 + species can induce the trapping of hole centers, and enhance the photoluminescence efficiency. More generally, these results enhance our understanding of REE structural and chemical roles in amorphous materials and increase our knowledge for technical applications.