5441436 | Journal of Non-Crystalline Solids | 2017 | 6 Pages |
Abstract
The refractive indices (n) and thermo-optic coefficients (ζ) of Ge14AsxSe86 â x and GexAs12Se88 â x glasses are measured in the 2-12 μm mid-infrared range. The composition dependences of the two parameters are investigated and strategies for tailoring them are proposed. The density (d) shows a maximum at the stoichiometric composition when Ge content is fixed; while it exhibits a minimum at the mean coordination number (< r >) of 2.67 when As concentration is fixed. The volume thermal expansion coefficient (β) broadly decreases with increasing < r >. Two semi-empirical relations are used to predict n and ζ from the glass composition. The n of a Ge-As-Se glass could be predicted with an error of < 1% from the d of the glass and the molar refractivity (Ri) of the constituent elements. The estimated values of Ri for Ge, As and Se between 2 and 12 μm range from 10.12-10.52, 11.71-11.91, and 11.17-11.25 cm3/mol, respectively. The ζ of a Ge-As-Se glass could be forecasted with an error of < 6 ppm/K from the β of the glass and the thermal coefficients of the molar refractivity (Ïi) of the constituent elements. The estimated values of Ïi for Ge, As and Se between 2 and 12 μm range from 26.2-26.7, 54.9-55.7 and 85.4-86.8 ppm/K, respectively.
Keywords
Related Topics
Physical Sciences and Engineering
Materials Science
Ceramics and Composites
Authors
Yuwei Wang, Sisheng Qi, Zhiyong Yang, Rongping Wang, Anping Yang, Pierre Lucas,