Enhanced visible-light photocatalytic activity of g-C3N4/TiO2 films

•Visible-light-driven g-C3N4/TiO2 composite films are successfully prepared.•The visible-light photo catalytic activity of TiO2 is remarkably improved by g-C3N4 loading.•The optimum g-C3N4 loading amount is about 50 wt%.•Enhanced activity is ascribed to the improved light harvesting of the g-C3N4/TiO2 composite.•Electron–hole separation process at the g-C3N4/TiO2 interface is proposed.

Enhanced photocatalytic degradation of methylene blue (MB) using graphitic carbon nitride/titanium dioxide (g-C3N4/TiO2) catalyst films has been demonstrated in this present work. The g-C3N4/TiO2 composites were prepared by directly heating the mixture of melamine and pre-synthesized TiO2 nanoparticles in Ar gas flow. The g-C3N4 contents in the g-C3N4/TiO2 composites were varied as 0, 20, 50 and 70 wt%. It was found that the visible-light-induced photocatalytic degradation of MB was remarkably increased upon coupling TiO2 with g-C3N4 and the best degradation performance of ∼70% was obtained from 50 wt% g-C3N4 loading content. Results from UV–vis absorption study, Electron microscopy, Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy suggest that the improved photoactivity is due to a decrease in band gap energy, an increased light absorption in visible light region and possibly an enhanced electron–hole separation efficiency as a result of effective interfacial electron transfer between TiO2 and g-C3N4 of the g-C3N4/TiO2 composite film. Based on the obtained results, the possible MB degradation mechanism is ascribed mainly to the generation of active species induced by the photogenerated electrons.

Graphical abstractFigure optionsDownload full-size imageDownload high-quality image (59 K)Download as PowerPoint slide