Effect of chain length and charge density on the construction of polyelectrolyte multilayers on colloidal particles

Two combinations of sodium poly(4-styrene sulfonate) (PSS) and poly(allylamine hydrochloride) (PAH) of different chain length and charge density are employed to construct multilayer films. The polyelectrolytes are assembled layer-by-layer on colloidal particles in the absence of salt. We have investigated the formation and electrical characteristics of the films by using electric light scattering technique. The results show that the film thickness is independent of the chain length when fully charged PAH (at pH 4.6) is combined with fully charged PSS. When the films are prepared with less charged PAH (at pH 6.7) and fully charged PSS, lower thickness is found for the film with shorter polymer chains. In all cases, the thickness increment realized on addition of the polymer with lower molar concentration is partially lost on exposure to the solution with higher concentration of the oppositely charged partner. When the film growth is regular (at equal molar concentrations of the fully charged polyelectrolytes), the ratio of PSS to PAH charge, estimated from the electro-optical effect values, exceeds 1. The electro-optical effect is also higher for the films ending with PSS when fully charged PSS is combined with less charged PAH (at pH 6.7). This reveals the key role of the charge in the last-adsorbed layer for the electro-optical behavior of the whole film.

Graphical abstractThe influence of charge density and chain length on formation of multilayer films from sodium poly(4-styrene sulfonate) and poly(allylamine hydrochloride) is investigated by electro-optics.Figure optionsDownload full-size imageDownload as PowerPoint slide