Abstract

In this study we developed composite coatings consisting of amorphous hydrogenated carbon (a-C:H) and molybdenum-disulfide (MoS2), and clarified their microstructure. In addition, we interpreted the tribological properties of the composite coatings in the viewpoint of a deposition-induced microstructural modification. The coatings were produced by the hybrid deposition technique of RF-generated methane and argon plasma and DC magnetron co-sputtering of MoS2 target. The deposition parameter investigated in this study was methane flow rate. Structural analyses were performed using a transmission electron microscope (TEM) and an atomic force microscope (AFM). Friction tests were conducted using a ball-on-disk type tribometer. From an electron micrograph, it was confirmed that nano-clusters were embedded into an amorphous carbon host matrix. Surface roughness of the composite coating was ∼ 0.25 nm in Ra compared to 5.0 nm in Ra of sputtered MoS2. The concentration measurements were performed, and the results show that the sulfur and molybdenum concentration ratio, [S]/[Mo], is ∼ 0.9, which indicates that the amount of sulfur was reduced due to the discharged plasma. In friction tests, composite coatings showed high friction in a vacuum condition. It was considered that lubricant MoS2 lamellar structures showing super-low friction in a vacuum condition during friction could not be formed between ball and coating during friction because of the lack of sulfur in embedded clusters.

Related Topics
Physical Sciences and Engineering Engineering Electrical and Electronic Engineering
Authors
, , , , ,