Nanocomposite membranes are fabricated from sodalite nanocrystals (Sod-N) dispersed in BTDA-MDA polyimide matrices and then characterized structurally and for gas separation. No voids are found upon investigation of the interfacial contact between the inorganic and organic phases, even at a Sod-N loading of up to 35 wt.%. This is due to the functionalization of the zeolite nanocrystals with amino groups (Si(CH3)(CH2)3NH2), which covalently link the particles to the polyimide chains in the matrices. The addition of Sod-N increases the hydrogen-gas permeability of the membranes, while nitrogen permeability decreases. Overall, these nanocomposite membranes display substantial selectivity improvements. The sodalite–polyimide membrane containing 35 wt.% Sod-N has a hydrogen permeability of 8.0 Barrers and a H2/N2 ideal selectivity of 281 at 25 °C whereas the plain polyimide membrane exhibits a hydrogen permeability of 7.0 Barrers and a H2/N2 ideal selectivity of 198 at the same testing temperature.