A sequentially coupling finite element analysis (FEA) program was utilized to simulate the stress field and calculate the diffused hydrogen concentration distribution of specimen exposed to the corrosion medium investigated. The FEA results indicated that corrosion pit affected the stress and diffusion hydrogen distribution around the corrosion pit where large stress gradients formed. Side surface cracks initiated from those corrosion pits and propagated under the synergy of stress and hydrogen. The effect of the corrosion pit on hydrostatic stress distribution was limited in superficial zone near the side surface, thus side surface cracks propagated along the hoop direction rather than along the direction of specimen thickness. Based on the morphology observation and FEA results, it can be concluded that the SCC mechanism of FV520B steel was hydrogen embrittlement mainly and combination of anodic dissolution. Simultaneously, corrosion pitting was the precondition of side surface crack formation while the stress induced hydrogen diffusion was the dominant factor.
Related Topics
Physical Sciences and Engineering
Chemistry
Electrochemistry
Authors
Renchao Wei, Xuedong Chen, Zhibin Ai, Youhai Jin,