Pr1.8La0.2Ni0.74Cu0.21Ga0.05O4+δ (PLNCG), a mixed ionic electron conductor (MIEC) with a K2NiF4-type structure, has been studied as a potential cathode material based on YSZ (ZrO2 with 8 mol% Y2O3) electrolyte for intermediate temperature solid oxide fuel cells (IT-SOFCs). The X-ray diffraction (XRD) analysis reveals that the good chemical compatibility between the PLNCG and YSZ. The maximum electric conductivity of the PLNCG appeared at about 460 °C and the value was 32 S cmâ1 in air and 34 S cmâ1 in O2, respectively. A hollow fiber SOFC was fabricated with the PLNCG as the cathode, NiO-YSZ (1:1; w/w) as the anode and YSZ as the electrolyte. The maximum power density of the cell is 876 mW cmâ2 and the corresponding polarization resistance of the cell is 0.41 Ω cm2 at 750 °C. Furthermore, the PLNCG cathode shows an excellent CO2 resistance in the operation temperature range. The maximum power density of the cell is similar to that when the cathode is exposed to air. Furthermore, the cell performance is stable when the CO2 concentrations in the air vary from 0 to 10 vol.% at both 700 and 750 °C. These results indicate that the PLNCG can be a good candidate for CO2 resistance cathode materials of IT-SOFCs based on YSZ electrolyte.
Keywords
Related Topics
Physical Sciences and Engineering
Chemistry
Electrochemistry
Authors
Shujun Peng, Yanying Wei, Jian Xue, Yan Chen, Haihui Wang,