To develop a technique for the mass production of beryllide pebbles, a crushing method for the granulation of beryllides was used in this study. Two types of crushed Be12Ti pebbles were prepared using mortar-ground (MG) and planetary-ball-milled (PM) powders. A granulation yield of approximately 50Â wt.% with sizes in the range of 0.85-1.18Â mm was achieved. Scanning electron microscopy (SEM) images revealed that the MG pebbles exhibited larger porosity because the larger size of the powder resulted in lower density with higher porosity. However, the considerably larger fraction of fine pores in the PM pebbles resulted in an increased Brunauer-Emmett-Teller (BET) specific surface area, as clearly demonstrated by high-magnification SEM images. To evaluate the reactivity with water vapor, the weight gain and H2 generation rate were also investigated. The results suggested that the PM pebbles exhibited notably lower reactivity, weight gain, and H2 generation rate, which may be due to the dramatically decreased BET specific surface. The fine pores were filled with stable oxides followed by a significant decrease of the surface area during oxidation. Optimization was performed to improve the circularity of the crushed pebbles. Grinding tests using planetary milling without balls for different times clearly demonstrated that the circularity improved (with an estimated value of 0.8) by cutting and polishing the sharp edges; however, long-duration milling for 99Â h resulted in attachment of the polished powders to the pebble surface, leading to surface color variation of the crushed pebbles.
Related Topics
Physical Sciences and Engineering
Energy
Nuclear Energy and Engineering
Authors
Jae-Hwan Kim, Masaru Nakamichi,