Mechanism for orientation dependence of blisters on W surface exposed to D plasma at low temperature

The orientation dependence of blister formation induced by D plasma exposure at low temperature (about 523 K) on rolled tungsten and chemical vapor deposition (CVD) W samples was studied by scanning electron microscopy and electron backscatter diffraction. Severe blistering was observed on grains with surface normal directions close to [111], while the [001] surfaces are the most resistant to blister formation. Cavities induced by D2 gas were observed beneath [111], [110] and [001] surfaces, independently on whether blisters were observed on the surface or not. The [111] surface is more prone to blister formation, because it is easily plastically deformed by the D2 gas pressure. Some blister edges and steps were perpendicular to [110] directions, which may be induced by the slipping of dislocations on {110} planes. The blister morphology induced by D plasma can be well explained by the blister model based on plastic deformation mechanism.