Microstructural changes in a neutron-irradiated Fe-15Â at.%Cr alloy

Microstructural changes in a Fe-15 at.%Cr model alloy neutron irradiated to 1.82 dpa at 290 °C were characterized by atom probe tomography. Homogenously distributed α′ precipitates as well as fewer clusters containing Si, P, Ni, and Cr, were observed in the matrix. Grain boundary analyses before and after irradiation revealed segregation of Cr, with W-shape concentration profiles developing in the vicinity of grain boundary carbide and nitride particles. After irradiation, impurities such as C, Si and P were segregated to the grain boundaries. Zones depleted of α′ clusters, and Si were found at the interfaces of carbide and nitride precipitates and along grain boundaries in the vicinity of these precipitates.