Abstract
The structural aspects of yttria-stabilized zirconia (YSZ) thermal barrier coatings grown on a polycrystalline alumina substrate have been studied as a function of annealing time at 1250â¯Â°C with the use of electron microscopy, X-ray diffraction, and Raman spectroscopy. Upon the high temperature exposure, the feathery morphology of the columnar grains of the as-deposited coatings smoothens out with the concurrent development of surface undulations and grain coarsening. It is shown that the grain coarsening results in significant voiding along the merged grain boundaries and inside YSZ grains. The nucleation and growth of the high density of voids is related to the clustering of vacancies supplied from the merged gaps between columnar grains and subgrains within the columnar grains. The continued development of the voids leads to the formation and propagation of large cracks within the columnar grains, which weakens the overall mechanical integrity of the coating.
Related Topics
Physical Sciences and Engineering
Materials Science
Nanotechnology
Authors
Yigen Fu, Caican Shao, Canying Cai, Yanguo Wang, Yichun Zhou, Guangwen Zhou,