Influence of Melt Spinning on the Electrochemical Hydrogen Storage Kinetics of RE-Mg-Ni-Based A2B7-Type Alloys

In order to improve the electrochemical characteristics of the La-Mg-Ni system A2B7-type electrode alloys, the partial substitution of M (M=Pr, Zr) for La has been performed. The melt spinning technology was used to prepare the La0.65M0.1Mg0.25Ni3.2Co0.2Al0.1 (M=Pr, Zr) electrode alloys. The influences of the melt spinning and substithting La with M (M=Pr, Zr) on the structures and the electrochemical hydrogen storage kinetics of the alloys were investigated. The results obtained by XRD and TEM reveal that the as-cast and spun alloys hold a multiphase structure, containing two main phases (La, Mg)2Ni7 and LaNi5 as well as a residual phase LaNi2. The as-spun (M=Pr) alloy displays an entire nanocrystalline structure, while an amorphous-like structure is detected in the as-spun (M=Zr) alloy, implying that the substitution of Zr for La facilitates the amorphous formation. The electrochemical measurement indicates that the high rate discharge ability (HRD) of the alloys first mounts up and then falls with rising of spinning rate. Furthermore, the electrochemical impedance spectrum (EIS), the Tafel polarization curves and the potential-step measurements all indicate that the electrochemical kinetics first increase and then decreases with growing of spinning rate.