Nd: YAG laser irradiation effects on structural and magnetic properties of Ni1+xZrxFe2-2xO4 nanoparticles

The effect of 112 mJ Nd: YAG laser irradiation on structural, morphological, infrared and magnetic properties of Ni1+xZrxFe2-2xO4 spinel ferrite nanoparticles has been systematically investigated in the present work. The sol-gel auto combustion synthesis method was successfully executed for the synthesis of the present system. All the samples were characterized by X-ray diffraction technique (XRD), scanning electron microscopy (SEM) and infrared spectroscopy (IR) technique. The magnetic properties of the present samples were measured by pulse field hysteresis loop technique. All the properties were measured for laser irradiated samples as well, to understand the effect of irradiation on the properties. The single-phase cubic spinel structure was confirmed by X-ray diffraction patterns of all samples and the disordered structure was observed for irradiated samples. The two principle absorption bands in IR spectra also confirm the formation of the spinel structure. Spherical and agglomerated morphology was observed for Zr4+ substituted nickel ferrite, whereas scratched morphology was observed for the irradiated samples. The grain size confirms the nanocrystalline nature, the crystallite size also evident the same. The magnetic parameters decreased after Zr4+ ion doping and strongly influenced by the irradiation.