A well-ordered and spherical LiNi0.6Co0.2Mn0.2O2 cathode material was successfully synthesized from Ni and Mn concentration-gradient precursors via co-precipitation. The crystal structure, morphology and electrochemical properties of LiNi0.6Co0.2Mn0.2O2 were characterized by X-ray diffraction, scanning electron microscopy, energy-dispersive spectroscopy, and charge–discharge tests. The material delivered an initial discharge capacity of 174.3 mAh/g at 180 mA/g (1 C rate) between 2.8 and 4.3 V and more than 93.1% of that was retained after 100 cycles. In addition, it also exhibited excellent rate capability, high cut-off voltage and temperature performance.
Graphical abstractSpherical and well-ordered layer-structured LiNi0.6Co0.2Mn0.2O2 cathode material with Ni and Mn concentration-gradient had been successfully prepared by a hydroxide co-precipitated method. The material delivers an initial discharge capacity of 174.3 mAh/g at 180 mA/g (1 C rate) between 2.8 and 4.3 V, more than 93.1% of that was retained after 100 cycles. Besides, it also exhibited excellent rate capability, high cut-off and temperature performance.Figure optionsDownload full-size imageDownload as PowerPoint slide