Crystal structure and some dynamic performances of Ti0.25V0.34Dy0.01Cr0.1Ni0.3 hydrogen storage electrode alloy have been investigated by XRD, FESEM-EDS, TEM and EIS measurements. The result shows that the alloy is mainly composed of V-based solid solution phase with body-centered-cubic structure and mono-crystal Ni3Ti phase with hexagonal structure (Space grope: P63/mmc), and it was first observed as TiNi-based secondary phase. The higher charge transfer resistance, higher apparent activation energy and lower hydrogen diffusion coefficient are reasons for the poor electrochemical activity of the dehydriding kinetics of Ti-V-Cr-Ni hydride alloy.