Thermal shock and post-quench strength of lapped borosilicate optical glass
Keywords: 61.43.Fs; 62.20.mj; 62.20.mm; 62.20.mt; 65.40.De; 81.40.Gh; Crack growth; Fracture; Strength; Defects; Borosilicates; Thermal shock;