The corrosion wear behaviour of selected stainless steels in potash brine

Tests were conducted at 25 and 85 °C to evaluate the corrosion wear resistance of selected stainless steels in potash brine using a reciprocating motion wear apparatus. Four materials were tested: Ferralium 255 (UNS S32550), AL6XN (UNS N08367), 254SMO (UNS S31254) and AISI 1018 (UNS G10180) for comparative purposes. The evaluation methods employed included weight loss analysis, optical microscopy and scanning electron microscopy (SEM). The results show that Ferralium 255 has superior corrosion wear resistance in potash brine environment compared to AISI 1018 plain-carbon steel and the other stainless steels tested. Wear surface analysis using SEM shows evidence of brittle fracture damage, which is attributed to the presence of Cl−.