A new lead alloy current-collector manufactured by a powder rolling process and its corrosion behavior under lead-acid battery conditions
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
شیمی
الکتروشیمی
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
A new powder rolling process for manufacturing current-collector sheets for lead-acid batteries has been developed. Gas-atomized lead-tin and lead-tin-calcium alloy powders obtained by a rapid solidification process in air were employed as raw materials for the powder rolling process. The corrosion behavior of powder-rolled lead-tin alloys with various compositions of tin has been investigated. A dipping corrosion test of square plain sheets of the alloys was performed in H2SO4 at 75 °C. The test was repeated up to 20 cycles with each cycle consisting of a controlled 10 mA cmâ2 oxidation current for 6 h and a rest under open circuit voltage for 6 h. The extent of corrosion-elongation and the appearance of the corroded surface of the tested specimens were the main observations. The corrosion-elongation of the corroded sheet of a powder-rolled lead alloy containing 1.5 wt% tin with ca. 200 μm initial thickness was less than 5%, whereas that of the corroded sheet of the cast-rolled lead alloy containing 1.5 wt% tin with the same initial thickness was 25-30% under the same corrosion test conditions. The corroded powder-rolled sheet of the 1.5 wt% tin lead alloy has uniform corrosion, but the cast-rolled sheet of lead alloy containing 1.5 wt% tin was much distorted and was perforated by the corrosion. Intergranular corrosion of the powder-rolled lead-tin alloys was much suppressed as compared with that of the cast-rolled lead-tin alloys.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Power Sources - Volume 185, Issue 1, 15 October 2008, Pages 559-565
Journal: Journal of Power Sources - Volume 185, Issue 1, 15 October 2008, Pages 559-565
نویسندگان
Masanori Sakai, Yasuo Kondo, Satoshi Minoura, Takeo Sakamoto, Tokiyoshi Hirasawa,