Yb3CoSn6 and Yb4Mn2Sn5: New polar intermetallics with 3D open-framework structures

Two new ternary ytterbium transition metal stannides, namely, Yb3CoSn6 and Yb4Mn2Sn5, have been obtained by solid-state reactions of the corresponding pure elements in welded tantalum tubes at high temperature. Their crystal structures have been established by single-crystal X-ray diffraction studies. Yb3CoSn6 crystallizes in the orthorhombic space group Cmcm (no. 63) with cell parameters of a=4.662(2), b=15.964(6), c=13.140(5) Å, V=978.0(6) Å3, and Z=4. Its structure features a three-dimensional (3D) open-framework composed of unusual [CoSn3] layers interconnected by zigzag Sn chains, forming large tunnels along the c-axis which are occupied by the ytterbium cations. Yb4Mn2Sn5 is monoclinic space group C2/m (no. 12) with cell parameters of a=16.937(2), b=4.5949(3), c=7.6489(7) Å, β=106.176(4)°, V=571.70(8) Å3, and Z=2. It belongs to the Mg5Si6 structure type and its anionic substructure is composed of parallel [Mn2Sn2] ladders interconnected by unusual zigzag [Sn3] chains, forming large tunnels along the c-axis, which are filled by the ytterbium cations. Band structure calculations based on density function theory methods were also made for both compounds.

Graphic abstractYb3CoSn6 and Yb4Mn2Sn5 have been prepared and structurally characterized. Yb3CoSn6 features a 3D open-framework composed of novel [CoSn3] layers interconnected by the zigzag Sn chains whereas the anionic substructure of Yb4Mn2Sn5 is composed of parallel [Mn2Sn2] ladders interconnected by the unusual one-dimensional (1D) chains formed by linear [Sn3] trimers.Figure optionsDownload as PowerPoint slide