A new direct route for the “bottom up” syntheses of phases in the Lan+1NinO3n+1 series (n=1, 2, 3 and ∞) has been achieved via single-step heat treatments of nanosized co-crystallized precursors. The co-crystallized precursors were prepared using a continuous hydrothermal flow synthesis system that uses a superheated water flow at ca. 400 °C and 24.1 MPa to produce nanoparticulate slurries. Overall, a significant reduction in time and number of steps for the syntheses of La3Ni2O7 and La4Ni3O10 was achieved compared with more conventional synthesis methods, which typically require multiple homogenization and reheating steps over several days.
Scanning electron micrograph of La4Ni3O10 (bar=1 μm) made by a single heat treatment at 1075 °C in air for 12 h of a 4:3 La:Ni ratio co-crystallite mixture of the metal hydroxides.Figure optionsDownload as PowerPoint slide
Journal: Journal of Solid State Chemistry - Volume 181, Issue 5, May 2008, Pages 1123–1132