More on the TR-OSL signal from BeO ceramics

• IR Stimulated Time-Resolved OSL from BeO was studied.
• Two components with lifetimes ∼2 and ∼17us were observed.
• IR stimulated TR-OSL signal is found to be stable up to 150 °C.
• Thermal quenching energy of the 2us component was found as 0.16 eV.

Time Resolved Optically Stimulated Luminescence (TR-OSL) from BeO ceramics was investigated using blue (445 nm) and near-IR light (852 nm) for stimulation. Stimulation spectrum of the TR-OSL signal – as measured in the interval 700 to 420 nm- was observed to increase monotonically with the decreasing stimulation wavelength. In addition to the “fast” and “slow” components observed with blue light stimulation, IR stimulated TR-OSL spectra of irradiated BeO ceramics were observed to have two components with average lifetimes around ∼2.5 μs and ∼17 μs. Emission spectra of the both IR stimulated TR-OSL components were observed to have a broad emission band peaking around 330 nm. Thermal stability of the IR stimulated TR-OSL signal was studied by making preheating experiments in the range from 100 °C to 190 °C. It was observed that the IR stimulated OSL signal is stable up to ∼150 °C and decay afterwards. Radiation dose response of the IR stimulated luminescence signal was obtained in the range from 5 to 500 Gy. Both blue and IR stimulated TR-OSL signals grew up to 100 Gy and exhibited saturation for higher doses. Additionally, measurement temperature dependence of the components was also investigated and for the ∼2 μs component thermal assistance with activation energy around 0.16 eV was observed. It seems that the fast component of the blue stimulated TR-OSL component can be correlated to the ∼2 μs IR stimulated TR-OSL component.