- Ti and TiZr implant surfaces are studied to further insight into osseointegration.
- Data are acquired from substrates subjected to SLA and SLActive surface treatments.
- All substrates exhibit surface films with near TiO2 stoichiometry.
- No evidence is found for discrete ZrOx phases on TiZr implant surfaces.
ObjectiveTargeting understanding enhanced osseointegration kinetics, the goal of this study was to characterize the surface morphology and composition of Ti and TiZr dental implant substrates subjected to one of two surface treatments developed by Straumann. These two treatments are typically known as SLA and SLActive, with the latter resulting in more rapid osseointegration.MethodsA range of techniques was applied to characterize four different substrate/surface treatment combinations (TiSLA, TiSLActive, TiZrSLA, and TiZrSLActive). Contact angle measurements established their hydrophilic/hydrophobic nature. Surface morphology was probed with scanning electron microscopy. X-ray diffraction, Raman μ-spectroscopy, and X-ray photoelectron spectroscopy were used to elucidate the composition of the near-surface region.ResultsConsistent with previous work, surface morphology was found to differ only at the nanoscale, with both SLActive substrates displaying nano-protrusions. Spectroscopic data indicate that all substrates exhibit surface films of titanium oxide displaying near TiO2 stoichiometry. Raman μ-spectroscopy reveals that amorphous TiO2 is most likely the only phase present on TiSLA, whilst rutile-TiO2 is also evidenced on TiSLActive, TiZrSLA, and TiZrSLActive. For TiZr alloy substrates, there is no evidence of discrete phases of oxidized Zr. X-ray photoelectron spectra demonstrate that all samples are terminated by adventitious carbon, with it being somewhat thicker (â¼1 nm) on TiSLA and TiZrSLA.SignificanceGiven previous in vivo studies, acquired data suggest that both nanoscale protrusions, and a thinner layer of adventitious carbon contribute to the more rapid osseointegration of SLActive dental implants. Composition of the surface oxide layer is apparently less important in determining osseointegration kinetics.
203
Journal: Dental Materials - Volume 33, Issue 1, January 2017, Pages 43-53