TiN modified SiC with enhanced strength and electrical properties
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
SiC based composites were manufactured with varying TiN content (0-50 V%) using Al2O3 and Y2O3 sintering aids. Basic dilatometry measurements were performed to determine when densification begins within the composite system. Samples were consolidated via uni-axial hot pressing at 1900 °C to produce ceramic composites with >98% theoretical density. Electrical measurements show increasing TiN additions reduce resistivity and begin to plateau at 40-50V%. Resistivity decreased from 2.0 Ã 105 Ω â cm (0% TiN) to 2.0 Ã 10â4 Ω â cm (50V% TiN). Flexural strengths were characterized and compared against a baseline (0% TiN) SiC. Strengths increased gradually with TiN content. A maximum strength 921 MPa was observed at 40V% TiN content vs. 616 MPa for the baseline SiC. This was a gain of 50% over baseline. Additions beyond that range did not produce further gains in strength.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of the European Ceramic Society - Volume 37, Issue 4, April 2017, Pages 1373-1378
Journal: Journal of the European Ceramic Society - Volume 37, Issue 4, April 2017, Pages 1373-1378
نویسندگان
Zachary N. Wing,