Phase transformation kinetics in rolled U-10 wt. % Mo foil: Effect of post-rolling heat treatment and prior γ-UMo grain size

The effect of sub-eutectoid heat treatment on the phase transformation behavior in rolled U-10 wt.% Mo (U10Mo) foils was systematically investigated. The as-cast 5 mm thick foils were initially homogenized at 900 °C for 48 h and were hot rolled to 2 mm and later cold rolled down to 0.2 mm. Three starting microstructures were evaluated: (i) hot + cold-rolled to 0.2 mm (as-rolled condition), (ii) hot + cold-rolled to 0.2 mm + annealed at 700 °C for 1 h, and (iii) hot + cold-rolled to 0.2 mm + annealed at 1000 °C for 60 h. Annealing of as-rolled materials at 700 °C resulted in small grain size (15 ± 9 μm average grain size), while annealing at 1000 °C led to very large grains (156 ± 118 μm average grain size) in rolled U10Mo foils. Later the samples were subjected to sub-eutectoid heat-treatment temperatures of 550 °C, 500 °C, and 400 °C for different durations of time starting from 1 h up to 100 h. U10Mo rolled foils went through various degrees of decomposition when subjected to the sub-eutectoid heat-treatment step and formed a lamellar microstructure through a cellular reaction mostly along the previous γ-UMo grain boundaries. The least amount of cellular reaction was observed in the large-grain microstructure at all temperatures. Conversely, a substantial amount of cellular reaction was observed in both the as-rolled and the small-grain microstructure. After 100 h of heat treatment at 500 °C, the volume fraction of the lamellar phase was found to be 4%, 22%, and 82% in large-grain, as-rolled, and small-grain samples, respectively.