Hexagonal Co/C/BaZn0.2Co0.8TiFe10O19 ternary hybrids: Synthetic method and microwave absorption properties
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
Hexagonal Co/C/BaZn0.2Co0.8TiFe10O19 ternary hybrids: Synthetic method and microwave absorption properties
چکیده انگلیسی
Through a simple method, hexagonal Co/C/BaZn0.2Co0.8TiFe10O19 ternary hybrids have been successfully prepared. The method can be used to prepare a variety of metal/ferrite. The saturation magnetization value gradually decreases with increasing content of BaZn0.2Co0.8TiFe10O19 (BZCTM). The coercivity value relates to particle size and content of BZCTM. The μ″-μ′ (μ′ and μ″ is the real and imaginary part of permeability respectively) curve can be used to infer the magnetic loss. For the materials mainly with magnetic loss, it can be used to infer the reflection loss. With d = 1.9 mm, the reflection loss (RL) of S1 (containing 0.1 g BZCTM) achieves minimum (−47.23 dB) at 9.95 GHz. For S4 (containing 0.7 g BZCTM), the bandwidth of RL below −10 dB is from 11 to 17.82 GHz (d = 1.9 mm). What's more, the μ″-μ′ curve can indicate the direction to improve magnetic loss, which is significance for studying the reflection loss of materials.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 731, 15 January 2018, Pages 515-523