The effect of hydroxyl groups and surface area of hematite derived from annealing goethite for phosphate removal

Synthetic goethite and thermally treated goethite at different temperatures were used to remove phosphate from sewage. The effect of annealing temperature on phosphate removal over time was investigated. X-ray diffraction (XRD), transmission electron microscopy (TEM), N2 adsorption and desorption (BET), and infrared emission spectrum (FT-IES) were utilized to characterize the phase, morphology, specific surface area, pore distribution, and the surface groups of samples. The results show that annealed products of goethite at temperatures over 250 °C are hematite with the similar morphology as the original goethite with different hydroxyl groups and surface area. Increasing temperature causes the decrease in hydroxyl groups, consequential increase in surface area at first and then experiences a decrease (14.8–110.4–12.6 m2/g) and the subsequent formation of nanoscale pores. The variation rate of hydroxyl groups and surface area based on FT-IES and BET, respectively, are used to evaluate the effect of annealing temperature on phosphate removal. By using all of the characterization techniques, it is concluded that the changes of phosphate removal basically result from the total variation rate between hydroxyl groups and surface area.

Figure optionsDownload high-quality image (63 K)Download as PowerPoint slideHighlights
► Much nanopore was formed during the thermal transformation of goethite to hematite.
► The variation of the numbers of hydroxyl groups was described by IES techniques.
► Same morphology and different surface area and hydroxyl groups for goethite and hematite.
► The decrease in hydroxyl groups not necessarily decreases the phosphate removal.
► Total variation rate of hydroxyl groups and surface area reflect the change of phosphate removal.