Microstructure evolution and tribological performance of Cu-WS2 self-lubricating composites
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی شیمی
شیمی کلوئیدی و سطحی
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Cu-WS2 self-lubricating composites containing various contents of WS2 were prepared by hot-pressing. The composite was also annealed at different temperatures to reveal the decomposition of WS2 during preparation. The influences of WS2 amount and annealing temperature on the phase, microstructure, hardness as well as friction and wear behaviors were investigated. The dry sliding wear of the composites against GCr15 steel ball was measured at the load of 10â¯N in atmosphere condition. The results revealed that the residual amount of WS2 decreased as the annealing temperature increased. The increase of hardness with the addition of WS2 was attributed to the interfacial reaction. Furthermore, the composite reinforced with 10â¯vol% WS2 exhibited a 71% reduction in the friction coefficient along with a promising 79% wear rate reduction, and an addition of 40â¯vol% WS2 resulted in even high wear resistance, with a 96% reduction in the wear rate. The tribological behavior of the composite was greatly influenced by the annealing temperature owing to the decomposition of WS2. Horizontal oriented WS2 sheets induced by friction were observed in tribolayer, and the related wear mechanism for the composites was discussed.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Wear - Volumes 412â413, 15 October 2018, Pages 109-119
Journal: Wear - Volumes 412â413, 15 October 2018, Pages 109-119
نویسندگان
Jin-Kun Xiao, Wei Zhang, Chao Zhang,