Transformation of sputtered calcium copper titanate thin film into nanorods by sequential annealing

Rapid synthesis of long calcium copper titanate (CCTO) nanorods was carried out by sequential annealing. CCTO thin films have been deposited on p-Si substrate by RF sputtering technique and afterwards, the samples were thermally treated using a preheated furnace by varying the annealing temperature from 850 °C to 1100 °C. CCTO nanorods of 12 µm lengths and 400-600 nm diameters were synthesized at 1100 °C. Based on the FESEM observations, a plausible growth mechanism has been proposed to explain the formation of nanorods. The (220) XRD peak of the CCTO film became prominent for the annealing temperature of 950 °C. The presence of nanoscale crystals in amorphous matrix has been observed by HRTEM studies. The elemental mapping of CCTO nanorod has shown a spatial variation of elements throughout the nanorod. The oxide and interface charge density was found to be increased with the rise in annealing temperature.