Investigation of high temperature annealing effectiveness for recovery of radiation-induced structural changes and properties of 18Cr-10Ni-Ti austenitic stainless steels

A complex study of structural state and properties of 18Cr-10Ni-Ti austenitic stainless steel after irradiation in BOR-60 fast research reactor (in the temperature range 330-400 °С up to damaging doses of 145 dpa) and in VVER-1000 light water reactor (at temperature ∼320 °С and damaging doses ∼12-14 dpa) was performed. The possibility of recovery of structural-phase state and mechanical properties to the level almost corresponding to the initial state by the recovery annealing was studied. The principal possibility of the recovery annealing of pressurized water reactor internals that ensures almost complete recovery of its mechanical properties and microstructure was shown. The optimal mode of recovery annealing was established: 1000 °C during 120 h.