Influence of TiN nanoparticles on the microstructure and properties of W matrix materials prepared by spark plasma sintering
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی انرژی
انرژی هسته ای و مهندسی
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
W-(0.5, 1, 2, 4) wt.% TiN composite powders were formed by mechanical alloying for 5 h and sintered by spark plasma at 1800 °C. The effect of TiN nanoparticle content on the microstructure and properties of the composites were investigated by scanning electron microscopy, transmission electron microscopy, tensile test, microhardness test, and thermal conductivity test. With the addition of TiN ranging from 0.5 wt.% to 4 wt.%, SEM analysis results showed that TiN was distributed homogeneously and W grains were refined by TiN. The fracturing of pure W was intergranular, whereas cleavage fracture appeared in the W-TiN composites and increased with increased TiN content. The density was found to initially increase and then decrease with increased TiN content. The same trend was observed for the thermal conductivity. Microhardness increased with increased TiN content. The tensile strength reached 180 MPa when the content of TiN was 2 wt.%. Furthermore, the mechanical properties of 2 wt.% exceeded those of other alloys at different TiN weight percentages.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Nuclear Materials - Volume 454, Issues 1â3, November 2014, Pages 114-118
Journal: Journal of Nuclear Materials - Volume 454, Issues 1â3, November 2014, Pages 114-118
نویسندگان
Shuang Wang, Lai-Ma Luo, Xiao-Yue Tan, Guang-Nan Luo, Xiang Zan, Ji-Gui Cheng, Xiao-Yong Zhu, Yu-Cheng Wu,