Temperature increase of Zircaloy-4 cladding tubes due to plastic heat dissipation during tensile tests at 0.1-10 s−1 strain rates

Limited temperature increases were measured at 0.1 s−1 strain rate. Limited but not strongly localized temperature increases were measured at 1 s−1. Large temperature increase were measured at 5 and 10 s−1 (142 °C at 5 s−1 strain rate in HT tests). The local temperature increase induced heterogeneous temperature fields, which enhanced strain localization and resulted in a reduction of the plastic elongation at fracture.