Environmental protection of Nb/Nb5Si3-based alloys by E/TBC systems

The lifetimes of the E/TBC systems exceeded the maximum exposure period of 1000 cycles at 1100 °C. When cyclically tested at 1200 °C, the samples with Ni-modified and boron containing Co-modified M7Si6-based bond coats failed within 700 cycles. Failure was caused by spallation of thick oxides scales thermally grown on the substrate after degradation of the bond coats. The E/TBC systems with boron containing Fe-modified M7Si6-based bond coats exhibited lifetimes approaching 1000 cycles at 1200 °C. For both YSZ and GZO topcoats, chemical reactions with the TGOs were observed.