Formation of nano iridium oxide: material properties and neural cell culture
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فناوری نانو (نانو تکنولوژی)
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Iridium film with the thickness of 30 and 60 nm were formed on both Si wafer and commercially pure (CP) Ti by electron beam evaporation. The thin iridium film showed the identical charge injection capability with the bulk Ir. However, the charge injection value of iridium film was decreased with continuous potential cycling when the deposited iridium became depleted due to the formation of oxide. The number of cycles at which the charge injection value decreased was 800 and 1600 cycles for the 30- and 60-nm-thick Ir film, respectively. FE-SEM observations on the cross section of Ir film clearly showed the thicker iridium oxide was formed with the more potential cycling. Ar ion beam etching to substrates before deposition certainly improved the adhesion strength of Ir film enough to resist to the strain induced by the larger volume occupation of iridium oxide. Swiss 3T3 fibroblasts culture on Ir and Ir oxide showed no cytotoxicity. Also, embryonic cortical neural cell culture on electrode indicated neurons adhered and survived by the formation of neurofilament.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Thin Solid Films - Volume 475, Issues 1â2, 22 March 2005, Pages 332-336
Journal: Thin Solid Films - Volume 475, Issues 1â2, 22 March 2005, Pages 332-336
نویسندگان
In-Seop Lee, Chung-Nam Whang, Young-Hee Lee, Gun Hwan Lee, Bong-Joo Park, Jong-Chul Park, Won-Seon Seo, Fu-Zhai Cui,