Synthesis and characterization of soluble polyimides based on a new fluorinated diamine: 4-Phenyl-2,6-bis[3-(4′-amino-2′-trifluoromethyl-phenoxy) phenyl] pyridine

A new kind of pyridine-containing aromatic diamine monomer, 4-phenyl-2,6-bis[3-(4′-amino-2′-trifluoromethyl-phenoxy) phenyl] pyridine (m-PAFP), was successfully synthesized by a modified Chichibabin reaction of 3-(4′-nitro-2′-trifluoro-methyl-phenoxy)-acetophenone with benzaldehyde, followed by a catalytic reduction. A series of fluorinated pyridine-bridged aromatic poly(ether-imide)s were prepared from the resulting diamine monomer with various aromatic dianhydrides via a conventional two-step thermal or chemical imidization method. The inherent viscosities values of these polyimides were in the range of 0.56–1.02 dL/g, and they could be cast and thermally converted into transparent, flexible, and tough polyimide films. The polyimides displayed higher solubility in polar solvents such as NMP, DMSO and m-cresol. The polyimides had good thermal stability, with the glass transition temperatures (Tg) of 187–211 °C, the temperatures at 5% weight loss of 511–532 °C, and the residue at 800 °C in air was higher than 50%. These films also had dielectric constants of 2.64–2.74 at 10 MHz and low water uptake 0.53–0.66%. Wide-angle X-ray diffraction measurements revealed that these polyimides were predominantly amorphous. Moreover, the polymer films of these novel polyimides showed outstanding mechanical properties with the tensile strengths of 90.1–96.6 MPa, elongations at breakage of 8.9–10.7% and tensile modulus of 1.65–1.98 GPa.

A series of fluorinated pyridine-bridged aromatic poly(ether-imide)s were prepared from a new kind of pyridine-containing aromatic diamine with various aromatic dianhydrides by two-step polycondensation method. The resulting polyimides exhibited good solubility in organic solvents, excellent thermal properties, and good mechanical properties, as well as low dielectric constants.Figure optionsDownload as PowerPoint slide