SANS from Pluronic P85 in d-water

Small-angle neutron scattering (SANS) has been used to investigate Pluronic P85 (EO26PO40EO26) copolymer in deuterated water. A range of P85 fractions were measured for a wide sample temperature window. A rich phase behavior is reported. Unimers were observed below the critical micelle formation condition. At fixed P85 fraction, a number of micellar phases were observed upon increasing temperature; first spherical micelles, then cylindrical micelles, then lamellar micelles. At the highest temperature, a demixed lamellae phase was observed. Analysis of the SANS data consisted in fits to an empirical Guinier–Porod model that was appropriate for data fitting in the various phases at low P85 fractions. When the P85 fraction increased, an inter-particle structure factor was included to analyze SANS data from concentrated spherical micelles. At high P85 fractions, paracrystalline structures were observed as evidenced by an enhanced inter-particle interaction peak. A phase diagram for P85/d-water was obtained showing the various phases. Focusing on the spherical micelles phase for one sample composition, a core-shell model was used to fit SANS data and obtain sizes and scattering length densities. Using material balance equations, information such as the aggregation number (i.e., number of Pluronic macromolecules per micelle) and the number of hydration water molecules in the shell region are determined.

Figure optionsDownload as PowerPoint slide