Single crystal of K3B6O10Cl with size of 35 mm × 35 mm × 11 mm was grown by the TSSG method for the first time. In the crystal growth process, the cooling rate, the rotating speed and seed direction have been investigated. Based on the measurement of refractive-index from UV to NIR region, the limit of type-I phase matching second harmonic generation wavelength was calculated to be 272 nm, which is a little shorter than that of LiB3O5 (277 nm). Thermal properties including specific heat, thermal diffusion and thermal conductivity were performed on the crystal. In addition, polarization measurements demonstrate that although K3B6O10Cl is polar, the material is not ferroelectric.
The crystal of K3B6O10Cl with sizes up to 35 mm × 35 mm × 11 mm was successfully grown by TSSG method. The preliminary measurements for linear, NLO optical and other functional properties have also been studied on the grown crystals. K3B6O10Cl is a potential UV NLO material for direct FHG of the 1112 nm laser.Figure optionsDownload as PowerPoint slide
Journal: Journal of Materiomics - Volume 1, Issue 3, September 2015, Pages 221–228