Formation of periodic structures by the space-selective precipitation of Ge nanoparticles in channel waveguides

Thermally stabilized channel waveguides with Bragg gratings were fabricated by the space-selective precipitation technique of crystalline Ge nanoparticles using KrF excimer laser irradiation. The periodic structures consisting of Ge nanoparticles were formed in Ge-B-SiO2 thin glass films after exposure to an interference pattern of the laser followed by annealing at 600 °C. The channel waveguides with the periodic structures were fabricated by the cladding of the patterned Cr layers on the films. The diffraction peak for the TE-like mode of 11.8 dB depth was observed clearly at a wavelength of 1526.4 nm, indicating that the periodic structure also served as the optical band-pass filter in optical communication wavelength. The spectral shape, diffraction efficiency, and diffraction wavelength remained unchanged even after annealing at 400 °C. Furthermore, a low temperature dependence of the diffraction wavelength - as low as 8.1 pm/°C - was achieved. The diffraction efficiency was further enhanced after subsequent annealing at 600 °C. The space-selective precipitation technique is expected to be useful for the fabrication of highly reliable optical filters or durable sensing devices operating at high temperature.