Electrolytical production of Ni + Mo + Si composite coatings with enhanced content of Si

Ni + Mo + Si composite coatings were prepared by co-deposition of nickel with molybdenum and silicon powders from a nickel solution in which Mo and Si particles were suspended by stirring. The layers have been deposited on a carbon steel substrate (St3S) under galvanostatic conditions. The content of Si in deposited layers was about 2-5 wt.% depending on deposition current density and the value of electric charge. For comparison Ni + Mo composite coatings were obtained under analogous current conditions. Composite coatings of enhanced Si content (15 wt.%) were deposited from an electrolyte in which 40 g/dm3 of Si covered with electroless plated nickel was dispersed. Deposition current density was equal 0.1 A/cm2 and the value of electric charge Q = 500 C/cm2. The thickness of the coatings was about 100-300 μm depending on their kind, electric charge and the deposition current density. Surface and cross-section morphology were investigated by scanning electron microscope (SEM). All deposited coatings are characterized by great, developed surface area. No internal stresses causing their cracking were observed. Chemical composition of the layers was determined by X-ray fluorescence spectroscopy (XRF) method and quantitative X-ray analysis (QXRD). It was stated, that the content of molybdenum and silicon in Ni + Mo + Si coatings depends on deposition current density and the amount of the powder in bath. The results of structural investigation of the obtained layers by the X-ray diffraction (XRD) method show, that they consist in crystalline Mo or Mo and Si phases built into Ni matrix. Moreover, Ni + Mo + Si composite coatings were modified by thermal treatment. It has been found that the thermal treatment of Ni + Mo + Si composite coatings caused that the new phases (NiSi, Mo2Ni3Si and Ni6Mo6C1.06) were obtained.