Observations on fretting damage transition to cracking; state of the art and preliminary observations

Interrupted fretting fatigue experiments were performed on 7075-T6 aluminum alloy and fretting damage characterized by confocal and scanning electron microscopy. Strain, induced by specimen fatigue, produces a small amplitude oscillatory motion between the fatigue specimen and the fretting pad. A fretting fatigue damage threshold exists in this material. Hundred percent fretting fatigue was defined as the average total cycles to fracture based on specimens 1-5 (both axial and normal forces were applied). Specimens had fretting damage induced at 100%, 80%, 60%, 40%, and 20% of the maximum fretting fatigue cycles to fracture. A positive correlation was not found between the depth of fretting damage and crack formation, but there appeared to be a stronger relationship between the fretting damaged surface areas, proximity of pits and crack nucleation sites.